Printing Instructions |
|
DuPont Teijin Films
|
Melinex® 313
|
Polyethylene Terephthalate (PET)
|
|
 |
| |
|
|
Description
|
Melinex® 313
is a polyeter
film similar to Melinex® S.
|
Applications
|
This grade of film is suitable for many applications. |
Pre-treatment
|
Pre-treated |
Approvals
|
None |
|
|
|
|
 |
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
um |
Micrometer
method
|
|
12
|
23
|
|
Thickness Gauge |
gauge |
|
|
48
|
92
|
|
Thickness
Thou |
" |
|
|
.0005
|
.0010
|
|
Yield |
Substance
Yield g/M2
|
g/M2
|
|
|
17
|
32
|
|
Yield
M2/ Kg |
M2/Kg |
|
|
59
|
31
|
|
Optical |
Haze |
% |
ASTM D 1003-77 |
Measured
on Gardner Hazemeter |
4.5 |
7.5 |
|
Total
luminious transmission
|
%
|
ASTM
D 1003-77
|
Measured
on Gardner Hazemeter
|
87.9 |
87.7 |
|
Mechanical
Properties MD |
Tensile Strength |
kgf/mm2 |
ASTM D 882-83
|
(12um
film 23°C at 50% r.h. Strain rate 50%/min) |
20 |
- |
|
Elongation
at break |
% |
ASTM D 882-83
|
(12um
film 23°C at 50% r.h. Strain rate 50%/min) |
125 |
- |
|
Mechanical
Properties TD |
Tensile Strength
|
kgf/mm2
|
ASTM D 882-83
|
(12um
film 23°C at 50% r.h. Strain rate 50%/min) |
26 |
- |
|
Elongation
at break
|
%
|
ASTM D 882-83
|
(12um
film 23°C at 50% r.h. Strain rate 50%/min) |
80 |
- |
|
Slip(coefficient of staticfriction)
|
kgf/mm2
|
ASTM
D1894-78
|
modified to Melinex method 12 um film |
0.4 |
- |
|
Thermal
Properties MD
|
Upper
melt temperature
|
°C
|
|
|
255
- 260
|
- |
|
Coefficient
of thermal expansion
|
1/K
(cm/cm deg) |
|
between
20 and 50°C
|
19
x 10 (pow -6)
|
- |
|
Shrinkage
|
%
|
|
after
5 minutes at 190°C
|
3 |
- |
|
Thermal
Properties TD
|
Upper
melt temperature
|
°C
|
|
|
255
- 260
|
- |
|
Coefficient
of thermal expansion
|
1/K
(cm/cm deg) |
ASTM
E794-85
|
between
20 and 50°C
|
16
x 10 (pow -6)(MD)
15x10
(pow -6)(TD) |
- |
|
Shrinkage
|
%
|
ASTM
E794-85
|
after
5 minutes at 190°C
|
3(MD)
3(TD) |
- |
|
Electrical
|
Breakdown Voltage |
kV |
ASTM D 149-81 |
(0.25 INCH ELECTRODES IN DRY AIR AT 25°c) |
4.8 |
6.4 |
|
Surface resistivity |
OHM/ |
ASTM D 257-83
|
(500V
at 20°C and 54% rh)
|
>10(pow.13)
|
|
|
Volume
Resistivity
|
ohm m
|
ASTM D 257-83
|
(100V
at 25°C and 100s)
|
10
(pow. 15)
|
|
|
Permittivity |
|
|
|
|
|
|
23°C,
50Hz |
|
ASTM D 150-81
|
|
3.26
|
|
|
23°C,
1KHz |
|
ASTM D 150-81 |
|
3.24
|
|
|
23°C,
10 KHz |
|
ASTM D 150-81 |
|
3.21
|
|
|
0°C,
50Hz |
|
ASTM D 150-81 |
|
3.26
|
|
|
50°C,
50Hz |
|
ASTM D 150-81 |
|
3.27
|
|
|
100°C,
50Hz |
|
ASTM D 150-81 |
|
3.35
|
|
|
150°C,
50Hz |
|
ASTM D 150-81 |
|
3.65
|
|
|
Power
Factor |
|
|
|
|
|
|
23°C,
50Hz |
|
ASTM D 150-81 |
|
0.002
|
|
|
23°C,
1Khz |
|
ASTM D 150-81 |
|
0.0055
|
|
|
23°C,
10Khz |
|
ASTM D 150-81 |
|
0.011
|
|
|
0°C,
50Hz |
|
ASTM D 150-81 |
|
0.004
|
|
|
50°C,
50Hz |
|
ASTM D 150-81 |
|
0.0015
|
|
|
100°C,
50Hz |
|
ASTM D 150-81 |
|
0.007
|
|
|
150°C,
50Hz |
|
ASTM D 150-81 |
|
0.006
|
|
|
Other |
|
|
| Other
Specifications: |
| |
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
Melinex® registered trademark
of DuPont Teijin Films. Only DuPont Teijin Films makes Melinex® brand polyester film |
|