®Hostaphan
|
RF
|
Polyethylene Terephthalate (PET)
|
|
 |
| |
| |
|
Description
|
Flame Retardant Film. A transparent film characterised
by excellent flame resistant properties. Good bonding strength
is achievable
with coatings,
printings and adhesive.
|
Applications
|
Flexible printed circuits, Membrance touch switches, cables,
protective clothing, protective overlay and electrical
insulations.
|
Pre-treatment
|
Optimised for high speed processing.
|
Approvals
|
none
|
| |
|
|
|
 |
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
um |
Micrometer
method
|
|
75 |
|
|
Thickness Gauge |
gauge |
- |
- |
300 |
|
|
Thickness
Thous |
" |
- |
- |
.0030 |
|
|
Yield |
Substance Yield G/M2 |
G/M2 |
- |
- |
105 |
|
|
Yield
M2/ Kg |
M2/Kg |
- |
- |
9.5 |
|
|
Optical
Properties |
Haze |
% |
ASTM D 1003-61
Method A |
-
|
value 18 |
|
|
Mechanical
Properties MD |
Tensile Strength |
N/mm2 |
ISO 527-1-2
|
Test
speed 100%/min
23°C,
50%r.h.
|
MD170 |
|
|
Elongation
at break |
% |
ISO 527-1-2
|
Test
speed 100%/min
23°C,
50%r.h. |
MD190 |
|
|
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO 527-1-2
|
Test
speed 100%/min
23°C,
50%r.h. |
TD 280 |
|
|
Elongation
at break |
% |
ISO 527-1-2
|
Test
speed 100%/min
23°C,
50%r.h. |
TD90 |
|
|
Thermal |
Shrinkage |
% |
DIN
40634
|
Test
condition 150°C, 15 MIN |
MD 1.0 |
TD
0.3
|
|
Surface |
Gloss
|
-
|
DIN 67530
|
value 150
|
Measuring
Angle 20°
|
|
|
Physical/Chemical |
Density
|
g/cm3
|
ASTM D 1505-68
Method C |
value
1.395
|
Test
Condition 23°C
|
|
|
Electrical
|
Dielectric constant
|
-
|
DIN 40634
|
value
3.3
|
1
kHz, 23°C
|
|
|
Dissipation factor
|
-
|
DIN 40634
|
value
0.0053
|
1
kHz, 23°C
|
|
|
Volume resistivity
|
ohms x cm
|
DIN 40634
|
value
10 to power of 17
|
23°C,
DC
|
|
|
Flame Retardancy
|
Consruction
|
-
|
DIN 4102
pt 1 + 2 |
value
B2**
value B1*** |
-
|
|
|
Public Transports
|
-
|
DIN 5510
|
value
S4
|
-
|
Class
|
|
|
|
-
|
DIN 5510
|
value
SR2
|
-
|
Smoke production
|
|
|
|
-
|
DIN 5510
|
value
ST2
|
-
|
Droplets
|
|
Aviation
|
-
|
-
|
value
Passed
|
Test Methods
FAR/JAR 25.853
|
-
|
|
|
-
|
-
|
value
Passed
|
FAR 25.853 |
Smoke
density
|
|
|
|
-
|
-
|
value
Passed
|
ABD 0031
|
Smoke
density
|
|
|
|
-
|
-
|
value
Passed
|
ABD 0031
|
Toxicity
|
|
|
|
-
|
-
|
value
Passed
|
App. F to part 1 (a),(1), (ii)
|
Vertical
Test (12s)
|
|
UL Test
|
-
|
-
|
value HB****
|
Test UL 94
|
|
|
LO1
|
%
|
-
|
value
30
|
ASTM-D 2863
|
|
|
**no flaming droplets, ***hardly combustible,
no flaming droplets, for inside and outside use, **** droplets,
no flaming, therefore
VTM is not applicable.
|
|
|
Other
|
Further excellent
properties are high mechanical strength, dimensional stability and
a glossy surface. The film can easily be coated or printed with
functional layers and is optimised for high speed processing. |
| |
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
| ®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |
|