Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
um |
Micrometer
method
|
|
36 |
75 |
190 |
Thickness Gauge |
gauge |
|
|
144 |
300 |
760 |
Thickness
Thous |
" |
|
|
.0014 |
.0030 |
.0075
|
Yield |
Substance Yield G/M2 |
G/M2 |
|
|
50 |
105 |
263 |
Yield
M2/ Kg |
M2/Kg |
|
|
20 |
9.5 |
3.8 |
Surface |
Coefficient of friction (static) |
- |
DIN
53375 or ASTM D 1894
|
Values
0.4
|
- |
-
|
- |
Surface
resistivity measured on RN 15**
|
ohms
|
DIN
53482 or VDE 0303/Part 3
|
value >5x10
to power of 14
|
23°C,
25%r.h.
|
-
|
-
|
Surface
resistivity measured on RN 15**
|
ohms
|
DIN
53482 or VDE 0303/Part 3
|
value >5x10
to power of 14
|
23°C,
50%r.h.
|
-
|
-
|
Surface
resistivity measured on RN 15**
|
ohms
|
DIN
53482 or VDE 0303/Part 3
|
value >5x10
to power of 14
|
23°C,
75%r.h.
|
-
|
-
|
Mechanical
Properties MD |
Tensile Strength
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD 200 |
MD
180
|
MD160 |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD 140 |
MD
160
|
MD
180 |
Tensile
Stress required to cause 5% elongation {F5 value}
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
MD
110
|
MD
110
|
MD110
|
Youngs
Modulus
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
MD
4000
|
MD
4000
|
MD3500
|
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
300 |
TD
280
|
TD260 |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
80 |
TD
80
|
TD
80 |
Tensile
Stress required to cause 5% elongation {F5 value}
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
TD
110
|
TD
110
|
TD
115
|
Youngs
Modulus
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
TD
5500
|
TD
5500
|
TD
5300
|
Thermal |
Shrinkage |
% |
DIN
40634
4000
|
150°C,
15 min |
MD1.0 |
1.0
|
1.0 |
|
% |
DIN
40634
4000
|
150°C,
15 min |
TD
0.3 |
0.3
|
0.3 |
Optical
|
Haze
|
|
|
|
Test Condition
|
|
|
36µ
|
%
|
ASTM D 1003-61 Method A
|
value 10
|
Enlarged measurement angle
|
-
|
-
|
75µ
|
%
|
ASTM D 1003-61 Method A
|
value 15
|
Enlarged measurement angle
|
-
|
-
|
190µ
|
%
|
ASTM D 1003-61 Method A
|
value 25
|
Enlarged measurement angle
|
-
|
-
|
Physical/Chemical
|
Density
|
g/cmx3
|
ASTM D 1505-68 Method C
|
value 1.395
|
Test 23°C
|
-
|
-
|
Frigen® extract
measured on RN 190
|
%
|
DIN 8944
|
value 0.05
|
Test -cold extraction
|
-
|
-
|
Conductivity of aqueous extract {all types}
|
µS/cm
|
DIN
40634 or 0345
|
value 2
|
Test 1kHz
|
-
|
-
|
Trichloroethylene
extract, measured on RN 190
|
%
|
DIN 8943
|
value 0.2
|
Test Extracted in Soxhlet-apparatus for 2h.
boiled down for 15h at 105°C
|
-
|
-
|
Water Absorption {compared to dry state, all
types}
|
%
|
DIN 53472 and ASTM D 570
|
value 0.5
|
Test Immersed in water for 4 days at 23°C
|
-
|
-
|
Barrier
|
Air
|
cm to power of 3/m to power of 2 x d x bar
|
DIN 53380
|
value 30
|
23°C
|
-
|
-
|
Oxygen
|
as above
|
DIN 53380
|
value 70
|
23°C
|
-
|
-
|
Water Vapour
|
g/m to power of 2 x d
|
DIN 53122
|
value 8
|
23°C
|
-
|
-
|
Nitrogen
|
cm to power of 3/m to power of 2 x d x bar
|
DIN 53380
|
value 20
|
23°C
|
-
|
-
|
Carbon Dioxide
|
as above
|
DIN 53380
|
value 240
|
23°C
|
-
|
-
|
Electrical
|
Dielectric
dissipation factor {tan8}
|
-
|
DIN 40634 or VDE 0345
|
value 0.0020
|
23°C;
50Hz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 0.0052
|
23°C;1
kHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 0.0210
|
23°C;
1MHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 0.0060
|
23°C;
240 MHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 0.0060
|
23°C;
9 300MHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 0.0048
|
150°C;
50Hz
|
-
|
-
|
Permittivity
|
-
|
DIN 40634 or VDE 0345
|
value 3.3
|
23°C;
50Hz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 3.3
|
23°C;1
kHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 3.2
|
23°C;
1MHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 2.9
|
23°C;
240 MHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 2.9
|
23°C;
9 300MHz
|
-
|
-
|
|
|
-
|
DIN 40634 or VDE 0345
|
value 3.6
|
150°C;
50Hz
|
-
|
-
|
Dielectric
strength measured on RN 25
|
kV/mm
|
DIN 40634 or VDE 0345 in air
|
value 510
|
23°C;DC
|
-
|
-
|
|
|
kV/mm
|
DIN 40634 or VDE 0345 in air
|
value 320
|
23°C;50Hz
|
-
|
-
|
|
|
kV/mm
|
DIN 40634 or VDE 0345 in air
|
value 135
|
150°C;50Hz
|
-
|
-
|
Dielectric
strength measured on RN 190
|
kV/mm
|
DIN 40634 or VDE 0345 in air
|
value 420
|
23°C;DC
|
-
|
-
|
|
|
kV/mm
|
DIN 40634 or VDE 0345 in air
|
value 150
|
23°C;50Hz
|
-
|
-
|
|
|
kV/mm
|
DIN 40634 or VDE 0345 in air
|
value 135
|
150°C;
50Hz
|
-
|
-
|
Volume
resistivity measured on RN 15**
|
ohms x cm
|
DIN 40634 or VDE 0345
|
value 10 to power of 18
|
23°C;DC
|
-
|
-
|
|
|
ohms x cm
|
DIN 40634 or VDE 0345
|
value 10 to power of 13
|
150°C; DC
|
-
|
-
|
** with small deviations for all thicknesses |
| |
| Range
of
Thickenesses: 36, 50, 75, 100, 125, 190, 250 and 350 microns |
| The
above data is typical of property values. |
| Other
Specifications: Industrial Applications, Decorative Films, Gloss
Laminations, Adhesive Tapes, Adhesive Films, Insulation Tapes,
Electrical Insulation, Reprography, Release Films, Stiffening
Applications, Building Insulations. |
| |
| |
| |
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |