Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
µm |
Micrometer
method
|
- |
12 |
19 |
- |
Thickness Gauge |
gauge |
- |
- |
48 |
76 |
- |
Thickness
Thous |
" |
- |
- |
.0005 |
.0007 |
-
|
Yield |
Substance Yield G/M2 |
G/M2 |
- |
- |
17 |
26 |
- |
Yield
M2/ Kg |
M2/Kg |
- |
- |
59 |
38 |
- |
Surface |
Coefficient of friction (static) |
- |
DIN
53375
|
Values
0.4
|
- |
-
|
- |
Surface
Tension
|
mN/m
|
DIN
53364
|
>50(6
months after delivery)
|
-
|
-
|
-
|
Mechanical
Properties MD |
Tensile Strength
|
N/mm2
|
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
230 |
MD
230
|
- |
Elongation
at break |
% |
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
110 |
MD
110
|
- |
Tensile
Stress required to cause 5% elongation {F5 value}
|
N/mm2
|
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h.
|
MD
110
|
MD
110
|
-
|
Youngs
Modulus
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
MD
4400
|
MD
5200
|
-
|
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
260 |
TD
260
|
- |
Elongation
at break |
% |
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
90 |
TD
90
|
- |
Tensile
Stress required to cause 5% elongation {F5 value}
|
N/mm2
|
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h.
|
TD
110
|
TD
110
|
-
|
Youngs
Modulus
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
TD5200
|
TD
5200
|
-
|
Thermal |
Shrinkage |
% |
DIN
40634 or VDE
0345
|
150°C,
15 min |
MD1.3 |
-
|
- |
|
% |
DIN
40634 or VDE
0345
|
150°C,
15 min |
TD
0.1 |
-
|
- |
Optical
|
Haze
|
-
|
-
|
-
|
Test Condition
|
-
|
-
|
12µ
|
%
|
ASTM D 1003-61 Method A
|
value
1.8
|
Enlarged
Measurement angle
|
-
|
-
|
19µ
|
%
|
ASTM
D 1003-61 Method A
|
value
2.2
|
Enlarged
Measurement angle
|
-
|
-
|
Physical/Chemical
|
Density
|
g/cmx3
|
ASTM
D 1505-68 Method C
|
value 1.395
|
Test 23°C
|
-
|
-
|
Barrier
|
Air
|
cm to power of 3/m to power of 2 x d x bar
|
DIN 53380
|
value
60
|
23°C
|
-
|
-
|
Oxygen
|
as above
|
DIN 53380
|
value
110
|
23°C,
50%r.h.
|
-
|
-
|
Water Vapour
|
g/m to power of 2 x d
|
DIN 53122
|
value
16
|
23°C,
85%r.h.
|
-
|
-
|
Nitrogen
|
cm to power of 3/m to power of 2 x d x bar
|
DIN 53380
|
value
35
|
23°C
|
-
|
-
|
Carbon Dioxide
|
as above
|
DIN 53380
|
value
500
|
23°C
|
-
|
-
|
|
Range
of
Thickenesses:12 and 19 microns |
| The
above data is typical of property values. |
| RNKC
complies wtih EC-Directive 90/128/ECC {latest version} as well
as with Recommendation XVII, polyterephthalic acid diolesters.
The film also complies with FDA Regulation 21 CFR 177.1630 |
| |
| |
| |
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |