Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
µm |
Micrometer
method
|
- |
36 |
55 |
65 |
Thickness Gauge |
gauge |
- |
- |
144 |
220 |
- |
Thickness
Thous |
" |
- |
- |
.0014 |
|
.0026
|
Yield |
Substance Yield G/M2 |
G/M2 |
- |
- |
50 |
|
92 |
Yield
M2/ Kg |
M2/Kg |
- |
- |
20 |
|
10.9 |
Mechanical
Properties MD |
Tensile Strength
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
180 |
MD 180
|
MD
180 |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
120 |
MD 150
|
MD
150 |
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
260 |
TD
260
|
TD
260 |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
80 |
TD
90
|
TD
90 |
Edge
tear resistance
|
N
|
DIN
40634
|
Test
speed 100%/min
23°C, 50%r.h.
|
TD
380
|
TD
380
|
TD
380
|
Puncture
resistance
|
N/mm2
|
Internal
measuring method
|
90° angle
with pin
|
350
|
350
|
350
|
Thermal |
Shrinkage |
% |
DIN
40634
|
150°C,
15 min |
MD1.0 |
MD
1.0
|
MD
1.0 |
|
% |
DIN
40634
|
150°C,
15 min |
TD
1.0 |
TD
1.0
|
TD
1.0 |
Melting
point
|
°C
|
Differential-
thermoanalysis
|
3
K/min
|
260
|
260
|
260
|
Optical
|
Haze
|
%
|
|
|
-
|
-
|
-
|
Transparency
36
|
%
|
ASTM
D 1003-61 Method A
|
400-900 nm
|
32
|
32
|
32
|
Transparency
55
|
%
|
ASTM
D 1003-61 Method A
|
400-900nm
|
28
|
28
|
28
|
Transparency
65
|
%
|
ASTM
D 1003-61 Method A
|
400-900nm
|
25
|
25
|
25
|
Transparency
36-65
|
%
|
ASTM
D 1003-61 Method A
|
250-360mm
|
0
|
0
|
0
|
Brightness
|
%
|
DIN 5033 or ASTM-D 1925-63T
|
|
60
|
60
|
60
|
Physical/Chemical
|
Density
|
g/cm3
|
ASTM
D 1003-61
|
23° C
|
1.43
|
1.43
|
1.43
|
Characteristic
odour
|
-
|
-
|
-
|
neutral
|
neutral
|
neutral
|
Barrier
|
Water
vapour permeability
|
g/m2
x d
|
DIN
53122
|
23° C
± 0.1 ° C 85% r.h.
|
6
|
3.5
|
3
|
Oxygen
permeability 36
|
cm3/m2
|
DIN 53380
|
23° C ± 0.1 ° C
53% r.h.
|
50
|
-
|
-
|
Oxygen
permeability 55
|
x
d x bar
|
DIN 53380
|
23° C ± 0.1 ° C
53% r.h.
|
-
|
35
|
-
|
Oxygen
permeability 36
|
|
DIN 53380
|
23° C ± 0.1 ° C
53% r.h.
|
-
|
-
|
25
|
Air
permeability 36
|
cm3/m2
|
DIN
53380
|
23° C ± 0.1 ° C
0 % r.h.
|
20
|
-
|
-
|
Air
permeability 55
|
x
d x bar
|
DIN
53380
|
23° C ± 0.1 ° C
0 % r.h.
|
-
|
6
|
-
|
Air
permeability 65
|
|
DIN
53380
|
23° C ± 0.1 ° C
0 % r.h.
|
-
|
-
|
5
|
Widths
on request. Other lengths on request |
Core
diameter: 152.4 mm (6") |
WD CSRE complies with EC-Directive
90/128/ECC (latest version) as well with Recommandation XV11, polyterephthalic
acid diolesters |
| |
| |
| |
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |