Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
um |
Micrometer
method
|
|
125 |
250 |
350 |
Thickness Gauge |
gauge |
|
|
500 |
1000 |
1400 |
Thickness
Thous |
" |
|
|
.0050 |
.0100 |
.0140
|
Yield |
Substance Yield G/M2 |
G/M2 |
|
|
175 |
357 |
500 |
Yield
M2/ Kg |
M2/Kg |
|
|
5.7 |
2.8 |
2 |
Physical/Chemical |
Conductivity
of the aqueous extract |
µS/cm |
DIN
40634 or VDE 0345
|
1
kHz
|
2 |
2
|
2 |
®Frigen extract
|
%
|
DIN
8944
|
Cold
extraction
|
0.05
|
0.05
|
0.05
|
Trichloroethylene
extract
|
%
|
DIN
8943
|
Extracted
in Soxhlet apparatus for 2 h. Boiled down: 15 h; 105° C
|
0.20
|
0.20
|
0.20
|
Mechanical
Properties MD |
Tensile Strength
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD 200 |
MD
200
|
MD
160 |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
180 |
MD
200
|
MD
230 |
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
290 |
TD
200
|
TD
180 |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
90 |
TD
170
|
TD
170 |
Thermal |
Shrinkage |
% |
DIN
40634
4000
|
150°C,
15 min |
MD
1 |
MD
1
|
MD
1 |
|
% |
DIN
40634
4000
|
150°C,
15 min |
TD
1 |
TD
1
|
TD
1 |
Electrical
|
Dielectric constant
|
-
|
DIN
40634
|
23° C;
50 Hz
|
3.3
|
3.3
|
3.3
|
Dielectric constant
|
-
|
VDE
0345 in air
|
23° C;1
kHz
|
3.3
|
3.3
|
3.3
|
Dielectric constant
|
-
|
ASTM-D
149
|
150° C;50
Hz
|
3.6
|
3.6
|
3.6
|
Dielectric
strength (WN 190)
|
kV/mm
|
DIN
40634
|
23° C;
DC
|
420
|
420
|
420
|
Dielectric
strength (WN 190)
|
kV/mm
|
VDE
0345 in air
|
23° C;
Hz
|
150
|
150
|
150
|
Dielectric
strength (WN 190)
|
kV/mm
|
ASTM-D
150
|
150° C;50
Hz
|
135
|
135
|
135
|
Dissipation
factor (tan)
|
-
|
DIN
40634
|
23° C;50
Hz
|
0.0020
|
0.0020
|
0.0020
|
Dissipation
factor (tan)
|
-
|
VDE 0345
in air
|
23° C;1kHz
|
0.0052
|
0.0052
|
0.0052
|
Dissipation
factor (tan)
|
-
|
ASTM-D
150
|
150° C;50
Hz
|
0.0048
|
0.0048
|
0.0048
|
Volume resistivity (WN 190)
|
ohms
x cm
|
DIN
40634
|
23° C;
DC
|
10
x(pow. 18)
|
10
x (pow.18)
|
10
x (pow.18)
|
Volume resistivity (WN 190)
|
ohms
x cm
|
VDE
0345 in air
|
150° C;
DC
|
10
x (pow.13)
|
10
x (pow.13)
|
10
x (pow.13)
|
Volume resistivity (WN 190)
|
ohms
x cm
|
ASTM-D
257
|
|
|
|
|
Surface
resistance (WN 190)
|
ohms
|
DIN
53482
|
23° C,
25% r.h.
|
>5
x 10(pow. 14)
|
<5
x 10 (pow.14)
|
<5
x 10 (pow.14)
|
Surface
resistance (WN 190)
|
ohms
|
VDE
0303/part 3
|
23° C,
50% r.h.
|
1
x 10 (pow.14)
|
1
x 10 (pow.14)
|
1
x 10 (pow.14)
|
Surface
resistance (WN 190)
|
ohms
|
und
ASTM-D 257
|
150° C,
75% r.h.
|
1
x 10 (pow.14)
|
1
x 10 (pow.14)
|
1
x 10 (pow.14)
|
Other
|
Behaviour
under the influence of partial discharges
|
min.
|
DIN
53485
|
Contact
method
|
900
|
900
|
900
|
Behaviour
under the influence of partial discharges
|
min.
|
VDE
0303/part 7
|
40
kV/mm
|
900
|
900
|
900
|
Hostaphan
WN is UL listed |
| |
| Range
of
Thickenesses: 125, 190, 230, 250, 300 and 350 micron |
| The
above data is typical of property values. |
| |
| |
| |
| |
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |