®Hostaphan
|
WO
|
Polyethylene Terephthalate (PET)
|
|
|
|
|
|
Description
|
A
white opaque film. It is noted for its very low transparency
and high brightness. It is therefore particularly suitable
as a versatile print medium offering outstanding
mechanical strength and dimensional stability .
|
Applications
|
Labels,
pre-paid cards, imaging e.g. ink jet film, high quality
alternative to paper e.g. for blilster packaging
|
Pre-treatment
|
Type
DO27 WO is uncoated.
Type
DO 27 E WO is treated on one side {aqueous inks}
Type
DO54 E WO is treated on one side {solvent based inks}
Type
DO27 B WO is treated on both sides {aqueous inks}
Type
054 B WO is treated on both sides {solvent based inks)
|
Approvals
|
none
|
|
|
|
|
|
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
µm |
Micrometer
method
|
- |
50 |
75 |
100 |
Thickness Gauge |
gauge |
- |
- |
200 |
300 |
400 |
Thickness
Thous |
" |
- |
- |
.0020 |
.0030 |
.0040
|
Yield |
Substance Yield G/M2 |
G/M2 |
- |
- |
71 |
105 |
141 |
Yield
M2/ Kg |
M2/Kg |
- |
- |
14 |
9.5 |
7.1 |
Surface |
Roughness
Ra value
|
nm
|
DIN
4762
|
value
40
|
cut-off 0.25
|
-
|
-
|
Gloss
|
-
|
DIN
67530
|
20
value
|
measuring
angle 20°
|
- |
|
Mechanical
Properties MD |
Tensile Strength
|
N/mm2
|
MD
140
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
140 |
MD
230
|
- |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
160 |
MD
110
|
- |
Tensile
Stress required to cause 5% elongation {F5 value}
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
MD
110
|
MD
90
|
-
|
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
230 |
TD
260
|
- |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
80 |
TD
90
|
- |
Tensile
Stress required to cause 5% elongation {F5 value}
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h.
|
TD
110
|
MD
110
|
-
|
Thermal |
Shrinkage |
% |
DIN
40634
|
150°C,
15 min |
MD1.0 |
-
|
- |
|
% |
DIN
40634
|
150°C,
15 min |
TD
1.0 |
-
|
- |
Optical
|
Lightness
50µm
|
-
|
DIN 5033
|
value
55
|
-
|
-
|
-
|
Lightness100µm
|
-
|
DIN 5033
|
value
40
|
-
|
-
|
-
|
Transparency
50µm
|
%
|
ASTM
D 1003-61 Method A
|
value
20
|
-
|
-
|
-
|
Transparency
100µm
|
%
|
ASTM
D 1003-61 Method A
|
value
10
|
-
|
-
|
-
|
Yellowness
Index
50µm
|
-
|
ASTM
D 1925 - 63T
|
value20
|
-
|
-
|
-
|
Yellowness
Index 100µm
|
-
|
ASTM
D 1925 - 63T
|
value
35
|
-
|
-
|
-
|
Physical/Chemical
|
Density
|
g/cmx3
|
ASTM
D 1505-68 Method C
|
value
1.42
|
Test 23°C
|
-
|
-
|
Product
Advantages
|
Suitable for all normal printing
processes (offset, flexographic, rotogravure and book printing).
Brilliant white surface for precise print reproduction. Outstanding
heat resistance. WO is available chemically treated on one or both
sides to assist adhesion to water or solvent based printing and
coating systems |
Range
of
Thickenesses: 50, 75, 100 125 micron |
The
above data is typical of property values. |
|
|
|
|
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |
|