Excell® XG562
|
Polyethylene Terephthalate (PET)
|
|
|
|
|
|
Description
|
Excell® XG562 Polyester Film is an Optically High Clear and both
sides chemically treated film, to promote good adhesion
to numerous solvent coatings and also to a wide range of
aqueous coatings.
|
Applications
|
Ssignificantly
improved metal adhesion, when aluminum metallized.
|
Pre-treatment
|
Chemically
treated both sides
|
Approvals
|
No
Approvals
|
|
|
|
|
|
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
um |
Micrometer
method
|
|
12 |
23 |
36 |
Thickness Gauge |
gauge |
|
|
48 |
92 |
144 |
Thickness
Thou |
" |
|
|
.0005 |
.001 |
.0014
|
Yield |
Substance
Yield g/M2 |
g/M2 |
|
|
17 |
32 |
50 |
Yield
M2/ Kg |
M2/Kg |
|
|
59 |
31 |
20 |
Optical
Properties |
Haze |
% |
ASTM D 1003 |
|
0.9 |
0.9
|
1.0 |
Mechanical
Properties MD |
Tensile Strength |
kgf/mm2 |
ASTM D 882A
|
|
26 |
25
|
23 |
Elongation
at break |
% |
ASTM D 882A
|
|
130 |
130
|
160 |
Young's Modulus
|
kgf/mm2
|
ASTM D 882A
|
|
450
|
450
|
450
|
Mechanical
Properties TD |
Tensile
Strength |
kgf/mm2 |
ASTM D 882A
|
|
25 |
24
|
24 |
Elongation
at break |
% |
ASTM D 882A
|
|
135 |
135
|
120 |
Young's
Modulus
|
kgf/mm2
|
ASTM D 882A
|
|
500
|
500
|
470
|
Shrinkage |
MD |
% |
TSI Method |
150 Deg
c/30 min |
1.5 |
1.5
|
1.0 |
TD |
% |
TSI Method |
150 Deg
c/30 min |
0.3 |
0.3
|
0.2 |
Other |
Total
Luminous Transmission
|
%
|
ASTM D 1003
|
|
90 |
90 |
90
|
Coefficient
of Friction
|
-
|
ASTM D 1894
|
Kinetic,
Chemical Side
|
0.4
|
0.4
|
0.4
|
Density |
g/cm3
|
ASTM D 1505
|
|
1.4
|
1.4
|
1.4
|
|
|
Other
Specifications: |
|
|
|
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
Excell® is the registered trademark
for Toray Saehan Inc |
|