Printing Instructions |
|
Toray Saehan
|
Excell® XP162
|
Polyethylene Terephthalate (PET)
|
|
 |
| |
|
|
Description
|
Excell® XP162 Polyester Fim is both sides chemically
treated packaging film. In the case of vacuum deposited
aluminium metallizing, the chemical treatment of XP162 promotes
enhanced metal adhesion.
|
Applications
|
Other side for aqueous coatings and lamination with adhesives.
|
Pre-treatment
|
Chemically Treated both side
|
Approvals
|
FDA STATUS: XP162 Polyester Film complies with the U.S.
Food & Drug Administration 21 CFR 177.1630 requirements
for food packaging applications.
|
|
|
|
|
 |
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
um |
Micrometer
method
|
|
9 |
12 |
16 |
Thickness Gauge |
gauge |
|
|
|
48 |
|
Thickness
Thou |
" |
|
|
|
.0005 |
|
Yield |
Substance
Yield g/M2 |
g/M2 |
|
|
|
17 |
|
Yield
M2/ Kg |
M2/Kg |
|
|
|
59 |
|
Optical
Properties |
Haze |
% |
ASTM D 1003 |
|
3.5 |
3.8
|
3.8 |
Mechanical
Properties MD |
Tensile Strength |
kgf/mm2 |
ASTM D 882A
|
|
27 |
26
|
26 |
Elongation
at break |
% |
ASTM D 882A
|
|
130 |
130
|
135 |
Young Modulus
|
kgf/mm2
|
ASTM D 882A
|
|
450
|
450
|
450
|
Mechanical
Properties TD |
Tensile
Strength |
kgf/mm2 |
ASTM D 882A
|
|
25 |
25
|
25 |
Elongation
at break |
% |
ASTM D 882A
|
|
130 |
135
|
135 |
Young Modulus
|
kgf/mm2
|
ASTM D 882A
|
|
500
|
500
|
500
|
Shrinkage |
Heat
Shrinkage MD |
% |
TSI Method
|
150
deg c / 30min |
1.4 |
1.4
|
1.4 |
Heat
Shrinkage TD |
% |
TSI Method
|
150
deg c / 30min |
0.3 |
0.3
|
0.3 |
Other
|
Total
Luminious Transmission
|
%
|
ASTM D 1003
|
|
89.7
|
89.6
|
89.6
|
Water
Vapour Transmission Rate |
g/m2
/ 24hour
|
ASTM
D F 372
|
37.8
deg c, 90%R.H.,1atm
|
56
|
43
|
35
|
Oxygen Permeability |
cc/m2
/ 24hour
|
ASTM D 3985
|
25
deg c, 75%R.H.,1atm
|
120
|
94
|
82
|
Surface
Tension |
dyne/cm
|
ASTM
D 2578
|
Corona
Treated Side
|
52
|
52
|
52
|
Density |
g/cm3
|
ASTM
D 1505
|
|
1.4
|
1.4
|
1.4
|
Other |
|
|
Other
Specifications: |
|
|
|
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
Excell® is the registered trademark
for Toray Saehan Inc. |
|