®Hostaphan
|
RUF
|
Polyethylene Terephthalate (PET)
|
|
|
|
|
|
Description
|
A
highly transparent film characterised by excellent flame
retardancy. Has a very high resistance against and high absorption
of UV radiation. Good bonding strength is achievable with coatings,
printings and adhesives. Further properties include hegh mechanical
strength, dimensional stability and glossy surface. |
Applications
|
Protective applications, agriculture, electrical
insulation, cables, clothing, protective overlay and outside
applications
|
Pre-treatment
|
Optimised
for high speed processing
|
Approvals
|
none
|
|
|
|
|
|
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
µm |
Micrometer
method
|
- |
19 |
- |
- |
Thickness Gauge |
gauge |
- |
- |
76 |
- |
- |
Thickness
Thous |
" |
- |
- |
.0007 |
.
- |
-
|
Yield |
Substance Yield G/M2 |
G/M2 |
- |
- |
26 |
- |
- |
Yield
M2/ Kg |
M2/Kg |
- |
- |
38 |
- |
- |
Surface |
Gloss
|
-
|
DIN
67530
|
180
value
|
measuring
angle 20°
|
-
|
-
|
Mechanical
Properties MD |
Tensile Strength
|
N/mm2
|
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
170 |
MD
230
|
- |
Elongation
at break |
% |
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
190 |
MD
110
|
- |
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
280 |
TD
260
|
- |
Elongation
at break |
% |
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
90 |
TD
90
|
- |
Thermal |
Shrinkage |
% |
DIN
40634
|
150°C,
15 min |
MD1.3 |
-
|
- |
|
% |
DIN
40634
|
150°C,
15 min |
TD
0.3 |
-
|
- |
Optical
|
Haze
|
%
|
ASTM
D 1003-61 Method A
|
value
3
|
-
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61
|
value>2
|
<360
nm, UV range
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61
|
value>75
|
390
nm, optical range
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61
|
value>85
|
500
nm, optical range
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61
|
value>85
|
1000
nm, IR range
|
-
|
-
|
Yellowness
Index
|
%
|
ASTM
D 1925 - 63T
|
value
3.0
|
-
|
-
|
-
|
Physical/Chemical
|
Density
|
g/cmx3
|
ASTM
D 1505-68 Method C
|
value 1.395
|
Test 23°C
|
-
|
-
|
Electrical
|
Dielectric
Constant
|
-
|
DIN
40634
|
value
3.3
|
test
1
kHz,23°C |
-
|
-
|
Dielectric
Factor
|
-
|
DIN
40634
|
value
0.0053
|
test
1
kHz,23°C |
-
|
-
|
Volume
Resistivity
|
ohms
x cm
|
DIN
40634
|
value
10 to power of 17
|
23°C,
DC
|
-
|
-
|
Flame Retardancy
|
Construction
|
-
|
DIN
4102 part 1 + 2
|
value
B2**value
B1***
|
-
|
-
|
-
|
UL
Test
|
-
|
UL94
|
value
HB****
|
-
|
-
|
-
|
LO1
|
%
|
ASTM
D 2863
|
value
33
|
-
|
-
|
-
|
**
no flaming droplets.
*** hardly combustible,
no flaming droplets,
for inside and
outside use. ****
droplets, no flaming,
therefore VTM is
not applicable. |
Other
|
RUF can easily be coated or printed
with functional layers. The film is optimised for high speed processing. |
Range
of
Thickenesses:19 micron |
The
above data is typical of property values. |
|
|
|
|
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |
|