®Hostaphan
|
RUHS
|
Polyethylene Terephthalate (PET)
|
|
|
|
|
|
Description
|
A
transparernt, biaxially orientated co-extruded film, with
two different surfaces. Characterised by very high resistance
against and high absorption of, UV radiation. One side is
modified to be heat sealable against PET and itself. Has
a high mechanical strength, dimensional stability and non-sealable
glossy surface.
|
Applications
|
Protective
applications against UV radiation. Outdoor applications.
Packaging and overlay panels and metal sheets. GRP applications.
|
Pre-treatment
|
Heat
Seal
|
Approvals
|
-
|
|
|
|
|
|
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
µm |
Micrometer
method
|
- |
20 |
- |
- |
Thickness Gauge |
gauge |
- |
- |
80 |
- |
- |
Thickness
Thous |
" |
- |
- |
.0008 |
.
- |
-
|
Yield |
Substance Yield G/M2 |
G/M2 |
- |
- |
28 |
- |
- |
Yield
M2/ Kg |
M2/Kg |
- |
- |
36 |
- |
- |
Mechanical
Properties MD |
Tensile Strength
|
N/mm2
|
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
210 |
-
|
- |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
MD
140 |
-
|
- |
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO-527-1-2
or VDE 0345
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
250 |
-
|
- |
Elongation
at break |
% |
ISO-527-1-2
|
Test
speed 100%/min
23°C, 50%r.h. |
TD
110 |
-
|
- |
Thermal |
Shrinkage |
% |
DIN
40634 or
VDE 0345
|
150°C,
15 min |
MD1.2 |
-
|
- |
|
% |
DIN
40634 or
VDE 0345
|
150°C,
15 min |
TD
0.2 |
-
|
- |
Optical
|
Haze
|
%
|
ASTM
D 1003-61 Method A
|
value
1.9
|
-
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61 Method A
|
value
0
|
<375
nm, UV range
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61 Method A
|
value>75
|
400
nm, optical range
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61 Method A
|
value>85
|
500
nm, optical range
|
-
|
-
|
Transparency
|
%
|
ASTM
D 1003-61 Method A
|
value>85
|
1000
nm, IR range
|
-
|
-
|
Physical/Chemical
|
Density
|
g/cmx3
|
ASTM
D 1505-68 Method C
|
value
1.4
|
Test 23°C
|
-
|
-
|
Remarks
|
RUF can easily be coated or printed
with functional layers. The film is optimised for high speed processing. |
Range
of
Thickenesses: 20 micron |
The
above data is typical of property values. |
|
|
|
|
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan is the registered
trademark for Mitsubishi Polyester Film GmbH. |
|